Water insoluble, insoluble, inorganic acid insoluble, soluble hydrofluoric acid and the nitric-acid mixed acid and degradation. It is strong in oxidation resistance, and easily melts and decomposes by potassium pyrosulfate. Superconductivity is demonstrated by its high conductivity. It can resist 30O at room temperatures.
Tantalum carbide This is useful for powder metallurgy as well as cutting tools for fine ceramics and chemical vapor deposition. It can also be used to make hardwear-resistant alloy cutting instruments, molds and additives for wear and corrosion resistance structural parts that improve the toughness and strength of alloys. Watch decoration can be made from the sintered body tantalum carbide.
Tantalum Carbide TaC Powder Properties | |
Additional Names | tantalum(IV) carbide, TaC powder |
CAS No. | 12070-06-3 |
Formula compound | TaC |
Molecular Weight | 192.96 |
Appearance | Powders from brown to deep brown |
Melting Point | 3850degC |
Boiling Point | 4780-5470 degC |
Density | 14.3-14.7g/cm3 |
Solubility in water | Unsolvable |
Get the exact Mass | 192.948 |
1. For TaC powder, use tantalum pentoxide and solid carbon ball mills. At 1700, reduce the mixture and then carburize in a nonoxidizing atmosphere (mainly vacuum, argon atmosphere).
2. By heat treating in an oxygen-free atmosphere using the liquid precursor, nano tantalum caride powder was made. A small glass beaker with 0.50gTaCL5 was filled with 5mL of anhydrousethanol. It was then stirred well using a glass rod. After it had been heated to 55°C and worked at 40kHz for 20 minutes, the ultrasonic cleaner turned on, and then put it into an 80-watt ultrasonic cleaner. The ultrasonic oscillation took between 5-10 minutes. Next, 0.10g was added to the nano-activated carbon. This oscillation continued for approximately 15-20 minutes. Then, pour it into the crucible. Coat it well on the inner wall. Dry it with a hot fan. Place the crucible and sample in a hot press furnace. High-temperature treatment took place at 1300 in a vacuum with 100Pa or hydrogen atmosphere. At 1400 in an atmosphere of argon, the holding time is 0.5h. Heating rate is 20/min. Use a brush to brush the product in the crucible after you have completed the experiment.
3. Tantalum pentoxide can be converted to heat by heating the air. Potassium pyrosulfate can be fused. Tantalum and tantalum carbon and tantalum pentoxide in an inert environment heated to 1900 reactions.
4. You can use tantalum pentoxide or methane to react gas. Argon as carrier. Silicon carbide resistance is required from external radiation heating and carbonization.
Tantalum Carbide TaC Powder
It is used widely in the military and industry. Cemented carbide is an example of a type additive. Its principal function is to inhibit the growth tungsten carbide particle formation and increase cemented carbidide’s high temperature strength.
Use as a coating on cutting tools to enhance the chemical resistance or wear resistance of base metal.
The military can use it to protect the blades of rocket engines and rocket nozzles. It will increase their resistance to ablative corrosion and can prolong their useful life.
Due to its high conductivity, you can use it as an electrode material by using electric wire cutting complex shapes.
The second phase of the particle-reinforced metal matrix composites can be used for aerospace, metallurgy as well as in other areas such electric power, waterpower, mining and other industries.
Major Supplier of Tantalum-Carbide TaC Powder
Technology Co. Ltd. (), is a trusted supplier of global chemicals and manufacturer. It has over 12-years experience providing high-quality chemical products. This includes silicon powder, nitride & graphite powders, zinc sulfide powders, calcium nitride, and 3D printing powders.
High-quality Tantalum carbide TaC powder, Please feel free to reach out and submit an inquiry. (brad@ihpa.net)